Alloy Type				Precious Metal Content %					Melting Range		Casting Temp.
	Application	Type	Color	Nl	Cr	Mo	Be	Co	°F	°C	°F	°C
DTX N.P.	5,6,11	PFM	WHITE	76	14	6	1.8	-	2250-2350	1232-1288	2500	1371
DTX N.P. (Be Free)	5,6,12	PFM	WHITE	77-78	11,12	3 or 4	-	-	2225-2250	1218-1232	2500	1371
DTX N.P. (Be & Ni Free)	5,6,12	PFM	WHITE	-	23	5.5	-	63	-	1370-1420	-	1470
RESPONSE	5,6,12	PFM	WHITE	72	20	8	-	-	2450	1343	-	1350
DTX NP SOFT	5,6,12	PFM	WHITE	67	13	13.2	1.31	<1	1150-1259	-	2700	-

Alloy Type	Density	Proof Stress (PSI)		Tensile Strength (PSI)		Elongation %		Vickers Hardness (DPH)		LASER WIRE	PRE	POST
	g/cm3	Soft	Hard	Soft	Hard	Soft	Hard	Soft	Hard
DTX N.P.	7.8	-	80,000 (CAST)	165,000 (CAST)	-	12-15 (CAST)	-	240 (CAST)	-	NPNI*	P,NP	LO,R
DTX N.P. (Be Free)	8.0	-	52,000 (CAST)	90,700 (CAST)	-	-	-	-	-	NPNI*	P,NP	LO,R
DTX N.P. (Be & Ni Free)	9.0	-	120,000 (CAST)	120,000	-	10	-	200 (CAST)	320	COCR	NP	LO,R
RESPONSE	7.8	-	56,000	70,000	-	9	9	320	190	NPNI*	NP	LO,R
DTX NP SOFT	8.09	-	-	895	-	3	-	-	-	NPNI*		LO,R

Alloy Type	Recommended Investment	Burn-out Temp. & 1 hr hold time +10 min. for each add. ring		Heat Treatment for 5 min. & bench cool		Degassing in Air or Otherwise Specified	Co-Eff. of Thermal Expansion
		°F	°C	°F	°C		25-500 °C	25-600 °C
DTX N.P.	Phosphate Bonded	1600	871	1200-1800	649-982	(Vacuum)	14	14.4
DTX N.P. (Be Free)	Phosphate Bonded	1600	871	1200-1800	649-982	(Vacuum)	13.7	14.3
DTX N.P. (Be & Ni Free)	Phosphate Bonded	1600	871	1200-1800	649-982	(Vacuum)	14.6	14.8
RESPONSE	Phosphate Bonded	1600	871	1200-1800	649-982	(Vacuum)	14.1	-
DTX NP SOFT	Phosphate Bonded	1800	-	1200-1800	649-982	(Vacuum)	12.83	-

APPLICATION:

1. Single-surface soft inlays.

2. Two-surface medium hard inlays M.O.D., and 3/4 crowns.

3. Full crowns, 3/4 crowns, M.O.D., bridge abutments and pontics, cat post, inlays, short and long-span bridges.

4. Heavy stress restorations: short and long-span bridges, implant over-structures, and cast partils.

5. Porcelain application: single unites, and short-span bridges.

6. Porcelain application: single-unites, hort, and long-span bridges.

7. Porcelain application: recommended for imlant over-structures.

8. Especially compatible with Vita porcelain.

9. Non-greening porcelains or non-greening liquids are recommended.

10. Recommended for high expansion, low fusing porcelains.

11. Porcelain application: very thin margins and Maryland bridges; designed for North American porcelains, ie. Ceramco II, Crystar.

12. Porcelain application: very thing margins and Maryland bridges; designed for European and Vita-type porcelains.

13. Single anterior units with fuyll porcelain coverage.