Alloy Type				Precious Metal Content %					Melting Range		Casting Temp.
	Application	Type	Color	Nl	Cr	Mo	Be	Co	°F	°C	°F	°C
DTX PDN (hard)	4	PARTIAL	WHITE	0.99	27	5.5	-	63.5	2480-2534	1360-1390	-	-
DTX PARTIAL	4	PARTIAL	WHITE	-	28	6	-	64	2372-2500	1300-1371	2750	1510
DTX NEOLOY 'N' (regular)	4	PARTIAL	WHITE	-	29.2	5.5	0	61.3	2580	1416	2750	1510
DTX ECONOMY (shot)	4	PARTIAL	WHITE	-	29	6	-	61	-	-	-	-
DTX WISIL	4	PARTIAL	WHITE	-	20	5	-	65	2475-2507	1355-1375	2795	1535

Alloy Type	Density	Proof Stress (PSI)		Tensile Strength (PSI)		Elongation %		Vickers Hardness (DPH)		LASER WIRE	PRE	POST
	g/cm3	Soft	Hard	Soft	Hard	Soft	Hard	Soft	Hard
DTX PDN (hard)	8.7	-	98,000 (CAST)	109,500 (CAST)	-	6 (CAST)	-	359 (CAST)	-	COCR*	WELDING RODS	-
DTX PARTIAL	8.3	-	80,000 (CAST)	109,000 (CAST)	-	10 (CAST)	-	380 (CAST)	-	COCR*	WELDING RODS	-
DTX NEOLOY 'N' (regular)	8.4	-	62,000 (CAST)	86,200	-	7.2	-	345 (CAST)	-	COCR*	WELDING RODS	-
DTX ECONOMY	-	-	-	-	-	-	-	-	-	COCR*	WELDING RODS	-
DTX WISIL	8.4	-	60,000 (CAST)	84,000	-	7	-	390 (CAST)	-	COCR*	WELDING RODS	-

Alloy Type	Recommended Investment	Burn-out Temp. & 1 hr hold time +10 min. for each add. ring		Heat Treatment for 5 min. & bench cool		Degassing in Air or Otherwise Specified	Co-Eff. of Thermal Expansion
		°F	°C	°F	°C		25-500 °C	25-600 °C
DTX PDN (hard)	Partial Investment	1700-1800	927-982	-	-	-	-	-
DTX PARTIAL	Partial Investment	1700-1800	927-982	-	-	-	-	-
DTX NEOLOY 'N' (regular)	Partial Investment	1700-1800	927-982	-	-	-	-	-
DTX ECONOMY	Partial Investment	1700-1800	927-982	-	-	-	-	-
DTX WISIL	Partial Investment	1700-1800	927-982	-	-	-	-	-

APPLICATION:

1. Single-surface soft inlays.

2. Two-surface medium hard inlays M.O.D., and 3/4 crowns.

3. Full crowns, 3/4 crowns, M.O.D., bridge abutments and pontics, cat post, inlays, short and long-span bridges.

4. Heavy stress restorations: short and long-span bridges, implant over-structures, and cast partils.

5. Porcelain application: single unites, and short-span bridges.

6. Porcelain application: single-unites, hort, and long-span bridges.

7. Porcelain application: recommended for imlant over-structures.

8. Especially compatible with Vita porcelain.

9. Non-greening porcelains or non-greening liquids are recommended.

10. Recommended for high expansion, low fusing porcelains.

11. Porcelain application: very thin margins and Maryland bridges; designed for North American porcelains, ie. Ceramco II, Crystar.

12. Porcelain application: very thing margins and Maryland bridges; designed for European and Vita-type porcelains.

13. Single anterior units with fuyll porcelain coverage.